Condensable light cure restorative composite
Use for filling cavities classes I and II by Black, capacity stump at microprosthetics, manufacturing tabs, creating lasting opaque layer in cosmetic restoration.
Radiopaque.
Composition and main characteristic
Microhybrid composite, curing when exposed to light with a wavelength of 400 - 500 nm. The curing depth at illumination with a 75 W lamp for 40 s is 3.5 - 6 mm.
It is prepared using a low-shrinkage formulation of an oligoether acrylate binder and traditional fillers for the LATELUX family. Thanks to the special technology of mixing the components of the composite paste, a high volume content of fillers (68.8%) was obtained while maintaining a sufficient degree of plasticity of the paste, which allows qualitative condensation of the paste in the carious cavity.
LATELUX MS has the minimum shrinkage (1.9 - 1.95% vol.), The highest microhardness (92 kg / mm2) and the strength at diametrical compression (59 MPa) among most other materials.
The material has good transparency (except opaque shades), does not stick to the instrument. The mono-component dentine-enamel light-curing adhesive Monotex, which is included in the system kit, provides reliable adhesion to cushion cement, phosphoric acid etched enamel and dentine. In the latter case, a special primer for dentin is required. Radiopaque.
Package:
- 5 g paste in a syringe
REF 1815 LATELUX MS, colour А2
REF 1810 LATELUX MS, colour А3
REF 1811 LATELUX MS, colour В2
REF 1812 LATELUX MS, colour ОА2
REF 1816 LATELUX MS, colour ОА3
REF 1813 LATELUX MS, colour ОА3,5
REF 1814 LATELUX MS, colour ОВ2